Characterization of bone material properties and microstructure in osteogenesis imperfecta/ brittle bone disease

by Jameson, John Robert, Ph.D., MARQUETTE UNIVERSITY, 2014, 175 pages; 3638886

Abstract:

Osteogenesis imperfecta (OI) is a genetic disorder primarily associated with mutations to type I collagen and resulting in mild to severe bone fragility. To date, there is very little data quantifying OI cortical bone mechanics. The purpose of this dissertation was to investigate bone microstructure, mineralization, and mechanical properties in adolescents with OI. Characterization studies were performed on small osteotomy specimens obtained from the extremities during routine corrective surgeries.

Nanoindentation was used to examine the longitudinal elastic modulus and hardness at the material level for mild OI type I vs. severe OI type III. Both modulus and hardness were significantly higher (by 7% and 8%, respectively) in mild OI cortical bone compared to the more severe phenotype. Lamellar microstructure also affected these properties, as the younger bone material immediately surrounding osteons showed decreased modulus (13%) and hardness (11%) compared to the older interstitial material.

A high resolution micro-computed tomography system utilizing synchrotron radiation (SRμCT) was described and used to analyze the microscale vascular porosity, osteocyte lacunar morphometry, and bone mineral density in OI vs. healthy individuals. Vascular porosity, canal diameter, and osteocyte lacunar density were all two to six times higher in OI cortical bone. Osteocytes were also more spherical in shape.

Finally, three-point bending techniques were used to evaluate the microscale mechanical properties of OI cortical bone in two different orientations. Elastic modulus, flexural yield strength, ultimate strength, and crack-growth toughness were three to six times higher in specimens whose pore structure was primarily oriented parallel vs. perpendicular to the long bone axis. There was also a strong negative correlation between the elevated vascular porosity of OI cortical bone and its elastic modulus, flexural yield strength, and ultimate strength. This relationship was independent of osteocyte lacunar density and tissue mineral density.

In summary, these findings highlight new material and microstructural changes within OI cortical bone that help contribute to its fragility. They also underscore a deep connection between bone structure and mechanical integrity at multiple length scales.

AdviserGerald Harris
SchoolMARQUETTE UNIVERSITY
Source TypeDissertation
SubjectsBiomedical engineering; Medical imaging; Biomechanics
Publication Number3638886

About ProQuest Dissertations & Theses
With nearly 4 million records, the ProQuest Dissertations & Theses (PQDT) Global database is the most comprehensive collection of dissertations and theses in the world. It is the database of record for graduate research.

PQDT Global combines content from a range of the world's premier universities - from the Ivy League to the Russell Group. Of the nearly 4 million graduate works included in the database, ProQuest offers more than 2.5 million in full text formats. Of those, over 1.7 million are available in PDF format. More than 90,000 dissertations and theses are added to the database each year.

If you have questions, please feel free to visit the ProQuest Web site - http://www.proquest.com - or contact ProQuest Support.