Thin film transistors (TFTs) are being used in a wide variety of applications such as image sensors, radiation detectors, as well as for use in liquid crystal displays. However, there is a conspicuous absence of interface electronics for bridging the gap between the flexible sensors and digitized displays. Hence is the need to build the same.

In this thesis, the feasibility of building mixed analog circuits in TFTs are explored and demonstrated. A flexible CMOS op-amp is demonstrated using a-Si:H and pentacene TFTs. The achieved performance is ≈ 50 dB of DC open loop gain with unity gain frequency (UGF) of 7 kHz. The op-amp is built on the popular 2 stage topology with the 2^nd stage being cascoded to provide sufficient gain. A novel biasing circuit was successfully developed modifying the g_m biasing circuit to retard the performance degradation as the TFTs aged.

A switched capacitor 7 bit DAC was developed in only nMOS topology using a-Si:H TFTs, based on charge sharing concept. The DAC achieved a maximum differential non-linearity (DNL) of 0.6 least significant bit (LSB), while the maximum integral non-linearity (INL) was 1 LSB. TFTs were used as switches in this architecture; as a result the performance was quite unchanged even as the TFTs degraded. A 5 bit fully flash ADC was also designed using all nMOS a-Si:H TFTs. Gray coding was implemented at the output to avoid errors due to comparator meta-stability. Finally a 5 bit current steering DAC was also built using all nMOS a-Si:H TFTs. However, due to process variation, the DNL was increased to 1.2 while the INL was about 1.8 LSB.

Measurements were made on the external stress effects on zinc indium oxide (ZIO) TFTs. Electrically induced stresses were studied applying DC bias on the gate and drain. These stresses shifted the device characteristics like threshold voltage and mobility. The TFTs were then mechanically stressed by stretching them across cylindrical structures of various radii. Both the subthreshold swing and mobility underwent significant changes when the stress was tensile while the change was minor under compressive stress, applied parallel to channel length.