Although NiTiNb alloys are well known as wide-hysteresis shape-memory alloys with important applications as coupling materials, the significance of one aspect of the Ni-Ti-Nb ternary system has not been fully appreciated. Based on the existence of a quasibinary NiTi-Nb eutectic isopleth in this ternary system, a novel braze method has been devised to fabricate metallurgical bonds between functional nitinol (NiTi) sections. When NiTi and pure Nb are brought into contact at temperatures above 1170°C, spontaneous melting occurs, forming a liquid that is extremely reactive and not only wets NiTi surfaces, but also apparently dissolves oxide scales, obviating the need for fluxes and providing for efficient capillary flow into joint crevices. The melting process is diffusion-controlled and rate-limited by the diffusivity of Nb in the liquid. The braze liquid will subsequently solidify into microstructures containing predominantly ordered NiTi and disordered bcc-Nb. Mechanical tests revealed that the braze joints are strong, ductile, and biocompatible. With appropriate post-braze aging, the functional performance of the parent NiTi alloy can be restored. Micro-alloying the Nb fluer metal with Zr or tungsten showed great potential for solution-strengthening of the braze joints. For applications where biocompatibility is not an issue, Nb metal can be substituted by pure vanadium as the braze filler, which is demonstrated to possess tensile strengths that can be potentially superior to the Nb counterparts.