Poly(ethylenimine) (PEI) is an ion conducting polymer with great potential for applications in lithium batteries and proton exchange membrane fuel cells. Branched poly(ethylenimine) was N-methylated via an Eschweiler-Clarke reaction to produce branched poly( N-methylethylenimine), BPMEI. Novel alkylated linear poly( N-ethylethylenimine), LPEEI, and linear poly(N-butylethylenimine), LPBEI, were synthesized from linear poly(ethylenimine), LPEI, via reductive amination of aliphatic aldehydes. Differential scanning calorimetry was used to determine the glass transition temperature, T_g, of neat BPMEI (T_g = -91°C), LPEEI (T_g = -80°C) and LPBEI (T _g = -50°C). T_gs of various N-alkylated PEI-lithium triflate complexes with different salt concentrations were determined. BPMEI exhibited a greater T_g change upon lithium triflate addition (from -91°C to 13°C) than that of LPMEI complexes (from -93°C to -14°C). It was found that LPEEI complexes showed higher T_gs at all salt concentrations than the corresponding LPMEI-LiSO₃CF₃ system. IR and Raman spectroscopy were used to study complexes of these polymers with lithium triflate for battery applications. Vibrational spectra of BPMEI-LiSO ₃CF₃ complexes revealed that aggregate formation is not observed until salt concentration reaches 5:1 (N:Li molar ratio). Additionally, a decrease in the relative concentration of "free" ions, compared to equivalent linear systems, was observed. LPEEI's spectra presented few changes upon salt addition, suggesting that salt addition causes less disruption of the local polymer microstructure than that observed in LPMEI systems in previous studies.

Linear poly(ethylenimine) hydrochloride, LPEİHCl, was successfully crosslinked using malonaldehyde generated in situ, and the degree of crosslinking was determined from the ratio of crosslink to polymer backbone hydrogens obtained using ¹H NMR spectroscopy. The ionic conductivity was highest at intermediate degrees of crosslinking ( ca. 0.45), approximately 1.0x10^-3 S/cm at room temperature and 75% relative humidity. IR and Raman spectroscopy were used to characterize the crosslinked network. The presence of β-amino-ethenyliminium crosslink units was identified through a series of bands between 1570 and 1640 cm ^-1. Ionic conductivity studies were performed on crosslinked LPEİHCl as a function of relative humidity, degree of crosslinking, temperature and phosphoric acid content. Results showed that the dependence of the conductivity on these factors is complex and that it involves a drastic transition in which the conductivity increases by several orders of magnitude. The onset of this transition appeared to be related to the composition of the polymer membranes. Membranes with ionic conductivities as high as 0.16 S/cm at 130ºC and 20% RH were obtained. Crosslinked LPEİHCl/H₃PO₄-based membranes were used in membrane electrode assemblies, MEAs, for proton exchange membranes fuel cells. MEAs were tested at temperatures ranging from 60 to 130°C and 30% RH. Upon comparison, LPEI-based MEAs exhibited better performance than Nafion® 117-based MEAs tested under the same conditions. PEI-based MEAs with 2.0 P:N and 0.66 degree of crosslinking produced 0.30 mA/cm ² at 0.38 V at 90°C and 30% RH. Nafion® 117-based MEAs produced 0.047 mA/cm² at 0.34 V under the same conditions.